FNQ Plastics Mechanical Strengths Data Sheets

 
Group 1
  PROPERTIES  POM POM PET PA6  PA6 PA6 PA6 PA PA PA6 PA PES PSU unit test met.
c h G  GHR  Goil  66:06:00 66 GF  11
1 Density 1.41 1.42 1.38 1.14 1.15 1.15 1.14 1.14 1.14 1.3 1.04 1.36 1.24 g/cm3 ISO.1183 
DIN.53479 
 
2 Water.absorption 0.2 0.2 0.2 2.8 2.4 2.2 1.5 2.6 2.6 2 0.9 0.8 0.3 % - 
in air  50% r.h.
 
3 Absorption 23°C in water-saturat. 0.7 0.7 0.5 9 7 6 4.8 8.4 8 5.2 2 2 0.6 % - 
  MECHANICAL  POM POM PET PA6  PA6 PA6 PA6 PA PA PA6 PA PES PSU      
PROPERTIES  c h G  GHR  Goil  66:06:00 66 GF  11
                   
4 Tensile stress 66 69 85 54 58 60 50 58 61 100 45 82 70 N/mm2 ISO.527 
at yeld at break -80 -85 -90 -70 -86 -88 -130 DIN.53455 
                 
5 Elongation 50 50 50 180 100 100 120 160 150 20 270 > 50 > 50 % ISO.527 
at break -60 -20 -20 -35 -45 -40 DIN.53455 
               
6 Tensile Modulus  2700 2900 3100 1700 1900 1900 1700 1800 (3100)  1900 (3200)  4000 1800 2600 2500 N/mm2 ISO.527 
of elasticity  -3000 -3400 -3500 -3100 DIN.53455 
           
7 Compressiontest  1% strain 1000h  14 14 20 6 7 6 6 7 7 15 4 20 13 N/mm2 ISO.899 
-18 -20 -20 -19 -20 -20  (28)  DIN.53444 
               
8 Impact strength  n.b. n.b. n.b. n.b n.b. n.b. n.b. n.b n.b n.b n.b n.b. n.b. KJ/ m2 ISO.R179 
Charpy   7,5 J  DIN.53453 
   
9 Notched impact  9 11 5 25 23 23 25 20 18 10 20 8 15 KJ/m2 ISO179/3C 
strength Charpy   -5 -5 -5 -8 -5 -5 DIN.53453 
               
10 Ball identation  140 150 170 80 100 100 80 100 100 170 100 150 140 N/mm2 ISO2039.1 
hardness  -155 -165 -170 -150 -170 -170 -210 DIN.53456 
                 
11 Rockwell  M88 M92 M95 M85 M88 M88 M82 M88 M89 M95 M83 M89 M69 - ISO2039.2 
hardness (dry) 
 
12 Coefficient of friction to steel    0.3 0.3 0.25 0.42 0.42 0.4 0.34 0.4 0.42 0.5 0.36 0.4 0.45 - - 
  THERMAL  POM POM PET PA6  PA6 PA6 PA6 PA PA PA6 PA PES PSU      
PROPERTIES  c h G  GHR  Goil  66:06:00 66 GF  11
                   
13 Melting  165 175 255 220 220 220 220 240 255 220 183 A A -  - 
point 
 
14 Thermal  0.3 0.3 0.28 0.25 0.28 0.28 0.28 0.26 0.25 0.25 0.23 0.18 0.26 W/(Km) DIN.52612 
conductivity 
 
15 Deformation at temp.HDT  115 135 95 83 96 96 90 88 103 150 55 195 174 °C ISO.75 
DIN.53461
 
16 Linear.expansion  110 110 70 90 80 80 80 85 85 50 100 60 60 10-6.K-1 - 
coeffic.23-60°C
 
17 Operating.temperature  continuously  110 100 115 88 100 100 100 92 95 105 85 180 150 °C - 
18 Operat.temperature  140 145 170 150 160 160 160 160 165 170 120 220 180 °C - 
short.period-no.load  
 
19 Min. operating  -50 -50 -20 -40 -30 -30 -30 -30 -30 -30 -50 -50 -50 °C - 
temperature 
 
20 Flammability UL 94  HB HB HB HB-  HB HB HB HB-  HB-  HB  V2 V0 HB - UL 94 
(3-6 mm thickness)  V2  V2 V2  V2  V2  V2
             
21 Oxigen index  15 15 22 24 25 25 25 27 25 24 22 38 32 % ISO.4589 
 (LOI ) 
 
  ELECTRICAL PROPERTIES  POM POM PET PA6  PA6 PA6 PA6 PA PA PA6 PA PES PSU      
c h G  GHR  Goil  66:06:00 66 GF  11
22 Dielectric constant  at 1 MHz. 3.8 3.7 3.2 7 7 7 7 8 7 7 4 3.6 3.1 - ISO.250 
-3.6 -3.7 -3.7 -3.7 -4 -3.6 -3.6 DIN.53483 
               
23 Dielectric strength 50 32 60 25 30 30 30 22 25 25 40 60 25 kV/ mm ISO.243 
DIN.53481 
 
24 Volume    1015 1015 1016 1012 1012 1012 1012 1012 1012 1012 1015 1017 51,016 Ohm.cm ISO.93 
resistivity  DIN.53482 
   
25 Dissipation.factor 0.01 0.01 0.01 0.06 0.05 0.05 0.05 0.06 0.06 0.06 0.05 0.01 0.02 - ISO.250 
 tan.d at 1MHz  DIN.53483 
   
 
Group 2
   PROPERTIES  PVDF PTFE PP PE 300 PE 500 PE PVC PC PPO ABS PEI  PPS PEEK unit test
1000 m  gf40  methods
1 Density 1.78 2.18 0.93 0.95 0.95 0.94 1.4 1.2 1.27 1.06 1.27 1.64 1.32 g/cm3 ISO.1183 DIN.53479
2 Water.absorption  0 0 0 0 0 0 0.1 0.2 0.1 0 0.2 0 0.1 % -
in air  50% r.h. 
 
3 Absorption 23°C in water-saturat. 0 0 0 0 0 0 0.1 0.4 0.3 0.7 1.2 0.1 0.5 % -
   MECHANICAL  PVDF PTFE PP PE 300 PE 500 PE PVC PC PPO ABS PEI  PPS PEEK    
PROPERTIES  1000 m  gf40 
       
4 Tensile stress  55 20 35 28 26 22 55 65 45 45 95 165 92 N/mm2 ISO.527 DIN.53455
at yeld at break 
 
5 Elongation  300 500 600 500 600 200 20 100 60 25 50 1 50 % ISO.527 DIN.53455
at break 
 
6 Tensile Modulus  2000 700 1100 900 800 780 2600 2300 2300 2500 3100 14000 3600 N/mm2 ISO.527 DIN.53455
of elasticity 
 
7 Compressiontest  1% strain 1000h  3 1.5 4 3 3 3 7 18 16 17 20 35 - N/mm2 ISO.899 DIN.53444
8 Impact strength  n.b. n.b. n.b. n.b. n.b. n.b. 15 n.b. n.b. n.b. n.b. 40 n.b. KJ/m2 ISO.R179 DIN.53453
Charpy   7,5 J 
 
9 Notched impact  7 14 7 30 50 80 4 23 15 14 80 8 80 KJ/m2 ISO.179/3C DIN.53453
strength Charpy  
 
10 Ball identation  100 30 75 55 50 40 75 110 100 85 170 400 - N/mm2 ISO.2039.1 DIN.53456
hardness 
 
11 Rockwell  R62 D53 R64 R60 R60 R60 M97 M75 M84 M82 M109 R123 M109 - ISO.2039.2 
hardness (dry) 
 
12 Coefficient of friction to steel    0.3 0.1 0.35 0.32 0.32 0.3 0 0.5 0.5 0.5 0.42 0.5 0 - -
  THERMAL  PVDF PTFE PP PE 300 PE 500 PE PVC PC PPO ABS PEI  PPS PEEK    
PROPERTIES  1000 m  gf40 
       
13 Melting  180 325 160 127 130 130 80 A  A A A 285 334 - -
point 
 
14 Thermal  0.11 0.24 0.4 0.4 0.4 0.4 0.15 0.21 0.22 0.15 0.22 0.2 0.25 W/ (Km) DIN.52612
conductivity 
 
15 Deformation at temp.HDT  95 50 65 50 50 50 60 135 130 85 195 260 160 °C ISO.75 DIN.53461
16 Linear.expansion  130 14 150 200 200 200 80 65 60 90 50 20 47 10-6.K-1 -
coeffic.23-60°C
 
17 Operating.temperature  continuously  140 250 90 80 80 80 60 120 90 90 180 230 230 °C -
18 Operat.temperature  155 260 110 95 95 100 65 135 105 100 200 260 300 °C -
short.period-no.load  
 
19 Min. operating  -50 -200 -10 -30 -30 -50 -5 -50 -20 -20 -30 -50 -50 °C -
temperature 
 
20 Flammability UL 94  V0 V0 HB HB HB HB HB HB  HB HB V0 V0 V0 - UL 94
(3-6 mm thickness)  V2 
   
21 Oxigen index  43 92 18 18 18 18 - 25 26 19 47 - 49 % ISO.4589 
 (LOI ) 
 
  ELECTRICAL PROPERTIES  PVDF PTFE PP PE 300 PE 500 PE PVC PC PPO ABS PEI  PPS PEEK    
1000 m  gf40 
22 Dielectric constant   8 2.1 2.2 2.3 2.3 2.3 3 3 3 3.3 3.2 4 3.3 - ISO.250 DIN.53483
at 1 MHz.
 
23 Dielectric  120 11 100 50 50 45 50 30 22 20 33 20 20 kV/ mm ISO.243 DIN.53481
strength 
 
24 Volume    1014 1015 1017 1017 1017 1017 1015 1016 1015 1016 71,015 1015 51,015 Ohm.cm ISO.93 DIN.53482
resistivity 
 
25 Dissipation.factor 0.06 0.0002 0.004 0.004 0.004 0.004 0.015 0.01 0.02 0.02 0.002 0.004 0.002 - ISO.250 DIN.53483
 tan.d at 1MHz 
 
       
Group 3  
  -  PROPERTIES  PVDF PTFE PP PE 300 PE 500  PE PVC  ABS - - unit   test       
1000 methods       
         
1 Density 1.78 2.18 0.93 0.95 0.95 0.94 1.4 1.06 - - g/cm3 ISO.1183 DIN.53479  
 
2 Water.absorption  0 0 0 0 0 0 0.1 0 - - % -  
in air  50% r.h.   
   
3 Absorption 23°C in water-saturat. 0 0 0 0 0 0 0.1 0.7 - - % -  
 
 -  MECHANICAL  PVDF PTFE PP PE 300 PE 500  PE PVC  ABS - - - -      
PROPERTIES  1000      
         
4 Tensile stress  55 20 35 28 26 22 55 45 - - N/mm2 ISO.527 DIN.53455  
at yeld at break   
   
5 Elongation  300 500 600 500 600 200 20 25 - - % ISO.527 DIN.53455  
at break   
   
6 Tensile Modulus  2000 700 1100 900 800 780 2600 2500 -   N/mm2 ISO.527 DIN.53455  
of elasticity   
   
7 Compressiontest  1% strain 1000h  3 1.5 4 3 3 3 7 17 - -- N/mm2 ISO.899 DIN.53444  
 
8 Impact strength  n.b. n.b. n.b. n.b. n.b. n.b. 15 n.b. - - KJ/m2 ISO.R179 DIN.53453  
Charpy   7,5 J   
   
9 Notched impact  7 14 7 30 50 80 4 14 - - KJ/m2 ISO.179/3C DIN.53453  
strength Charpy    
   
10 Ball identation  100 30 75 55 50 40 75 85 - - N/mm2 ISO.2039.1 DIN.53456  
hardness   
   
11 Rockwell  R62 D53 R64 R60 R60 R60 M97 M82 - - - ISO.2039.2   
hardness (dry)   
   
12 Coefficient of friction to steel    0.3 0.1 0.35 0.32 0.32 0.3 0 0.5 - - - -  
 
- THERMAL  PVDF PTFE PP PE 300 PE 500  PE PVC  ABS - - - -      
PROPERTIES  1000      
         
13 Melting  180 325 160 127 130 130 80 A - - - -  
point   
   
14 Thermal  0.11 0.24 0.4 0.4 0.4 0.4 0.15 0.15 - - W/ (Km) DIN.52612  
conductivity   
   
15 Deformation at temp.HDT  95 50 65 50 50 50 60 85 - - °C ISO.75 DIN.53461  
 
16 Linear.expansion  130 14 150 200 200 200 80 90 - - 10-6.K-1 -  
coeffic.23-60°C  
   
17 Operat.temperature  continuously  140 250 90 80 80 80 60 90 - - °C -  
 
18 Operat.temperature  155 260 110 95 95 100 65 100 - - °C -  
short period no load    
   
19 Min. operating  -50 -200 -10 -30 -30 -50 -5 -20 - - °C -  
temperature   
   
20 Flammability UL 94  V0 V0 HB HB HB HB HB HB - - - UL 94  
(3-6 mm thickness)   
   
21 Oxigen index  43 92 18 18 18 18 - 19 - - % ISO.4589   
 (LOI )   
   
- ELECTRICAL PROPERTIES  PVDF PTFE PP PE 300 PE 500  PE PVC  ABS - - - -      
1000      
       
22 Dielectric constant   8 2.1 2.2 2.3 2.3 2.3 3 3.3 - - - ISO.250 DIN.53483  
at 1 MHz.                  
   
23 Dielectric  120 11 100 50 50 45 50 20 - - kV/ mm ISO.243 DIN.53481  
strength   
   
24 Volume    1014 1015 1017 1017 1017 1017 1015 1016 - - Ohm.cm ISO.93 DIN.53482  
resistivity   
   
25 Dissipation.factor 0.06 0.0002 0.004 0.004 0.004 0.004 0.015 0.02 - - - ISO.250 DIN.53483  
 tan.d at 1MHz   
       
 
-  Figures relate to specimen conditioned at 23°C and 50% RH.  Figures between brackets (   ) relate to dry specimen. Figures for materials marked with * can change according to their  moisture content..
-  Figures  refer to un-coloured specimen either injection moulded or machined in the easiest way. Tests made on specimen of different sizes give slightly different results. 
12 Test on ground steel dry specimen  load =0,05 N/mm2     speed =0,6 m/s.  
15 Deformation at temperature. HDT  at 1,8 N/mm2 
17 Operating temperature  continuously  5000h From 23 °C upwards  the materials' features change in an ununiform and disproportional way due to the heat. The quoted limits are indicative and based on a tensile stress of 50% of the value at 23° C.
18 Operating temperature short period (no load) 
19 The mechanical features decrease with a reduction in temperature and are influenced also by other factors (moisture , etc. ). The quoted value does not take into consideration impact conditions or heavy loads. 
A amorphous
- All values and information provided are based on information currently in our possesion and/or results acheived from tests  conducted in our laboratories . They are given in good faith and are not legally binding . For any   particular application , the technical staff of FNQ Plastics are at your disposal to assist with solving  your problem.